Effect of a polymerization inhibitor on the chemomechanical properties and consistency of experimental resin composites

Abstract This study investigated the effect of butylated hydroxytoluene (BHT) inhibitor on degree of conversion (DC), flexural strength (FS), flexural modulus (FM), Knoop microhardness (KH), microhardness reduction (HR), and consistency of experimental resin composites at different BHT concentrations: C0 (control-0%); C0.01 (0.01%); C0.025 (0.025%); C0.05 (0.05%); C0.1 (0.1%); and C0.5 (0.5%). For the consistency, the composites were tested immediately after being exposed to a dental chair headlight (0, 20, 40 and 60 s). Data concerning DC, FS, FM, KH, and HR were submitted to one-way ANOVA, while the consistency data was submitted to 2-way ANOVA; mean values were then compared (Tukey's test; α=0.05). The KH, FS and FM analyses showed no significant difference among the composites tested. For DC, C0 showed the highest mean value (74.2%) and differed only from C0.5 (67.2%). For HR, C0.5 showed the lowest mean (13.09%) value and differed from C0 (26.4%) and C0.01 (24.87). The consistency analysis showed no difference among C0.05, C0.1 and C0.5, considering 0 and 20 s of light exposure, while C0 (14.07 mm), C0.01 (13.97 mm), and C0.025 (14.18 mm) showed higher mean values at 0 s when compared to 20 s (12.67, 12.77 and 13.05 mm, respectivelly). Polymerization occurred within 40 s of light exposure for C0, C0.01, C0.025, and C0.05 and within 60 s for C0.1. In conclusion, the BHT concentrations had no significant influence on FS, FM and KH. The higher the BHT concentration, the longer was its handling time under light, with a significant improvement in the HR, but a decrease in DC. Therefore, BHT at 0.1% showed the best outcomes concerning all the BHT concentrations tested.

Resumo O objetivo foi investigar o efeito do inibidor de polimerização BHT no grau de conversão (GC), resistência à flexão (RF), módulo de flexão (MF), microdureza Knoop (KH) e redução da microdureza (RKH), e consistência de um compósito experimental contendo diferentes concentrações de BHT (% em peso): C0 - controle (0%); C0,01 (0,01%); C0,025 (0,025%); C0,05 (0,05%); C0,1 (0,1%); e C0,5 (0,5%). Para o teste de consistência, os compósitos foram testados imediatamente após serem expostos à luz de um refletor odontológico por 0, 20, 40 e 60 s. Os dados relativos a GC, RF, MF, KH e RKH foram submetidos a one-way ANOVA, enquanto os dados de consistência foram submetidos a two-way ANOVA; os valores médios foram comparados (teste de Tukey; α = 0,05). As análises de KH, RF e MF não mostraram diferença significativa entre os compósitos testados. Para GC, C0 apresentou o maior valor médio e diferiu apenas de C0,5. Para a RKH, C0,5 apresentou o menor valor médio e diferiu de C0 e C0,01. A análise de consistência não mostrou diferença entre C0,05, C0,1 e C0,5, considerando-se 0 e 20 s de exposição à luz, enquanto C0, C0,01 e C0,025 apresentaram maiores valores médios a 0 s quando comparados a 20 s. A polimerização ocorreu dentro de 40 s de exposição à luz para C0, C0.01, C0.025 e C0.05 e dentro de 60 s para C0.1. Em conclusão, as concentrações de BHT não tiveram influência significativa sobre RF, MF e KH. Quanto maior a concentração de BHT, maior o tempo de manuseio sob luz, com melhora significativa da RKH, mas diminuição da GC. Portanto, o compósito contendo 0,1 % de BHT apresentou os melhores resultados entre as demais concentrações testadas.

Polymerization capability of simplified dental adhesives with camphorquinone, phenyl-propanedione and bis-alkyl phosphine photoinitiators

Aim: this study aimed to evaluate the degree of conversion (DC) exhibited by novel formulations of dental adhesive systems including camphorquinone (CQ), phenyl-propanedione (PPD), and bis-alkyl phosphine oxide (BAPO) when cured by mono- or polywave light emitting diodes (LEDs). Methods: an adhesive model was formulated by mixing hydroxyethyl methacrylate (HEMA, 40 wt%) and bisphenol A glycidyl dimethacrylate (BisGMA, 60 wt%) in ethanol (30 wt%). Five materials were then formulated by adding the following photoinitiators: CQ (1 mol%), CQ/PPD (0.5/0.5 mol%), CQ/BAPO (0.5/0.5 mol%), PPD (1 mol%), and BAPO (1 mol%). The DC for each material was measured with Fourier transform infrared spectroscopy. Analysis of variance and Tukey's post-hoc test were used to analyze the data (p < 0.05). Results: Except for CQ, the photoinitiators provided a significantly higher DC in the adhesive systems following photoactivation with a polywave LED. Conclusion: The use of alternative photoinitiators and a polywave LED improved the DC of the adhesive systems examined

Influence of Different Concentration and Ratio of a Photoinitiator System on the Properties of Experimental Resin Composites

Abstract The aim in this study was to evaluate the influence of different ratio of camphorquinone/tertiary amine concentration on the flexural strength (FS), elastic modulus (EM), degree of conversion (DC), yellowing (YL), water sorption (WS) and water solubility (WSL) of experimental composites. Thus, acrylate blends were prepared with different camphorquinone (CQ) and amine (DABE) concentrations and ratios by weight: (CQ/DABE%): 0.4/0.4% (C1), 0.4/0.8% (C2), 0.6/0.6% (C3), 0.6/1.2% (C4), 0.8/0.8% (C5), 0.8/1.6% (C6), 1.0/1.0% (C7), 1.0/2.0% (C8), 1.5/1.5% (C9), 1.5/3.0% (C10). For the FS and EM, rectangular specimens (7x2x1 mm, n=10) were photo-activated by single-peak LED for 20 s and tested at Instron (0.5 mm/min). Then, the same specimens were evaluated by FTIR for DC measurement. For YL, disks (5x2 mm, n=10) were prepared, light-cured for 20 s and evaluated in spectrophotometer using the b aspect of the CIEL*a*b* system. For WS and WSL, the volume of the samples was calculated (mm³). For WS and WSL, composites disks (5x0.5 mm, n=5) were prepared. After desiccation, the specimens were stored in distilled water for 7 days and again desiccated, in order to measure the WS and WSL. Data were submitted to one-way ANOVA and Tukey's test (5%). The groups C8, C9 and C10 showed higher DC, EM and YL means, compared to other composites. Therefore, the FS and WS values were similar among all groups. Also, C1, C2 and C3 presented higher WSL in 7 days, compared to other composites. In general, higher concentrations of camphorquinone promoted higher physical-mechanical properties; however, inducing higher yellowing effect for the experimental composites

Resumo O objetivo foi avaliar a influência da concentração e proporção de canforoquinona (CQ)/amina terciária (DABE) na resistência à flexão (RF), módulo flexural (MF), grau de conversão (GC), amarelamento (AM), sorpção (SA) e solubilidade em água (SL) de compósitos experimentais. Blendas acrilatas foram preparadas com diferentes concentrações e proporções de CQ/DABE em peso, como segue: (CQ/DABE%): 0,4/0,4% (C1); 0,4/0,8% (C2); 0,6/0,6% (C3); 0,6/1,2% (C4); 0,8/0,8% (C5); 0,8/1,6% (C6); 1,0/1,0% (C7); 1,0/2,0% (C8); 1,5/1,5% (C9); 1,5/3,0% (C10). Para RF e MF, espécimes retangulares (7x2x1 mm, n=10) foram fotoativados com LED de pico único (Radii Cal) por 20 s e testados em máquina Instron (0,5 mm/min). Após, o GC dos mesmos espécimes (fragmentos) foi mensurado por FTIR. Para AM, discos de compósito (5x2 mm, n=10) foram preparados, fotoativados por 20 s e imediatamente avaliados em espectrofotômetro, considerando o aspecto b do sistema CIEL*a*b*. Para SA e SL, discos de compósito (5x0,5 mm, n=5) foram preparados e seus volumes calculados (mm³). Após desidratação, as amostras foram pesadas e armazenadas em água destilada por 7 dias, pesadas e novamente desidratadas e pesadas, para se calcular o SA e SL. Os dados foram submetidos a one-way ANOVA e teste de Tukey (5%). Os grupos C8, C9 e C10 mostraram maior GC, MF e AM, comparado aos outros grupos. No entanto, RF e SA foram similares entre todos os grupos. Ainda, C1, C2 e C3 apresentaram maior SL em 7 dias comparado aos outros grupos. Em geral, maiores concentrações de CQ promoveram melhores propriedades físico-mecânicas; no entanto, levaram ao maior amarelamento dos compósitos.

Evaluation of phenyl-propanedione on yellowing and chemical-mechanical properties of experimental dental resin-based materials

ABSTRACT Objective To evaluate the influence of phenyl-propanedione on yellowing and chemical-mechanical properties of experimental resin-based materials photoactivated using different light curing units (LCUs). Material and Methods Experimental resin-based materials with the same organic matrix (60:40 wt% BisGMA:TEGDMA) were mechanically blended using a centrifugal mixing device. To this blend, different photoinitiator systems were added in equimolar concentrations with aliphatic amine doubled by wt%: 0.4 wt% CQ; 0.38 wt% PPD; or 0.2 wt% CQ and 0.19 wt% PPD. The degree of conversion (DC), flexural strength (FS), Young’s modulus (YM), Knoop hardness (KNH), crosslinking density (CLD), and yellowing (Y) were evaluated (n=10). All samples were light cured with the following LCUs: a halogen lamp (XL 2500), a monowave LED (Radii), or a polywave LED (Valo) with 16 J/cm2. The results were analysed by two-way ANOVA and Tukey’s test (α=0.05). Results No statistical differences were found between the different photoinitiator systems to KNH, CLS, FS, and YM properties (p≥0.05). PPD/CQ association showed the higher DC values compared with CQ and PPD isolated systems when photoactivated by a polywave LED (p≤0.05). Y values were highest for the CQ compared with the PPD systems (p≤0.05). Conclusion PPD isolated system promoted similar chemical and mechanical properties and less yellowing compared with the CQ isolated system, regardless of the LCU used.

The effect of shade and curing mode on cure efficiency of dual-cure resin cements / Efeito da cor e do modo de cura na eficiência de cura de cimentos resinosos de cura dual

Objective: To evaluate the effect of shade and curing mode on cure efficiency of two dual-cure resin cements. Material and Methods: Two shades (A2 and TRANS) of two different dual-cure resin cements (G-CEM, GC Dental and SET PP, SDI) were submitted to different curing modes: light curing through a 2 mm thick ceramic disc (IPS Empress Esthetic, A2, Ivoclar Vivadent) for 20 s (16 J/cm2), 40 s (32 J/ cm2) or 80 s (64 J/cm2) performed immediately or with 1 or 5 min of delay. Fourier transform infrared spectroscopy (FT-IR) was used to evaluate the degree of conversion (DC) after 48 h. For the statistical analysis, data were submitted to threeway analysis of variance, followed by Tukey’s test for multiple comparisons (p<0.05). Results: Shade influenced DC (%) for the dual-cure resin cements tested (p=0.00001). TRANS shade showed lower DC (%) for both cements when there was no delay before light-curing (p=0.00001). Curing mode also influenced DC (%) for the dual-cure resin cements tested: radiant exposure greater than 32 J/cm2 and delaying light-curing for 1 to 5 min increased the DC (%) for both dual-cure resin cements evaluated. Conclusions: One minute delay prior to light-curing improved the cure efficiency and may be a more clinically acceptable approach to increase the degree of conversion of dual-cure resin cements.

Objetivo: Avaliar a influência da cor e do modo de polimerização no grau de conversão de dois cimentos resinosos duais. Material e Métodos: Duas cores (A2 e TRANS) de dois cimentos resinosos duais (G-CEM, GC Dental e SET PP, SDI) foram submetidos a diferentes modos de cura: fotoativação através de um disco de cerâmica de 2 mm de espessura (IPS Empress Esthetic, A2, Ivoclar Vivadent) por 20 s (16 J/cm2), 40 s (32 J/cm2) ou 80 s (64 J/cm2) realizada imediatamente ou após 1 ou 5 min de espera. Espectrometria com transformada de Fourier (FT-IR) foi utilizada para avaliação do grau de conversão (GC) após 48 h. Para a análise estatística, os dados foram submetidos à análise de variância com três fatores, seguida de teste de Tukey para comparações múltiplas (p=0.05). Resultados: A cor influenciou o GC (%) dos cimentos resinosos duais avaliados (p=0.00001). A cor TRANS resultou menor GC (%) para ambos os cimentos quando não houve espera antes da fotoativação (p=0.00001). O modo de cura também teve influência n o GC (%) dos cimentos resinosos duais avaliados: doses de energia superiores a 32 J/cm2 e espera de 1 ou 5 min antes da fotoativação aumentou o GC (%) dos dois cimentos resinosos duais avaliados. Conclusão: Um min de espera antes da fotoativação melhorou a eficiência de cura e pode ser uma abordagem clinicamente aceitável para aumentar o grau de conversão de cimentos resinosos duais.

Effect of Low Shrinkage Monomers on Physicochemical Properties of Dental Resin Composites

The aim of this study was to evaluate the effect of low shrinkage monomers on physicochemical properties of dental resin composites. Two low shrinkage resin composites: one with a crosslink branching monomer (Kalore, GC Corp) and a novel monomer (Venus Diamond, Heraeus Kulzer) were compared to a conventional resin composite formulation (Filtek Z250, 3M/ESPE). The volumetric shrinkage was evaluated by µCT analysis (n=5) and the physicochemical properties by degree of C=C conversion (DC), flexural strength (FS) and Young's modulus (YM) (n=10). All samples were light cured by a LED device (Radii, SDI) with 16 J/cm2. The results were analysed by one-way ANOVA and Tukey test for multiple comparisons (α=0.05). No statistical difference was found between µCT shrinkage values to Kalore (1.8%) and Venus Diamond (1.7%) (p≥0.05); Z250 presented statistical highest shrinkage value (2.0%). Kalore presented higher statistical DC (60.8%) than Venus Diamond (49.5%) and Z250 (49.6%). No statistical difference was found between FS or YM properties to Venus Diamond and Z250; Kalore presented statistical lowest FS and YM properties (p≥0.05). Conclusion: Using novel monomers seem to reduce polymerization shrinkage without affecting the physicochemical properties evaluated of resin composites rather than using crosslink branching monomers.

O objetivo deste trabalho foi avaliar o efeito de monômeros de baixa contração de polimerização nas propriedades físico-químicas de resinas compostas. Duas resinas de baixa contração de polimerização com monômeros do tipo crosslink (Kalore GC Corp) ou do tipo novelar (Venus Diamond Heraeus Kulzer) foram comparadas a uma resina composta convencional (Filtek Z250 3M/ESPE). A contração de polimerização foi avaliada através da análise por µCT (n=5) e as propriedades físico-químicas através da análise do grau de conversão C=C (GC) resistência flexural (RF) e módulo de Young (MY) (n=10). Todas as amostras foram fotoativadas com uma fonte de LED (Radii SDI) com 16 J/cm2. Todos os resultados foram submetidos aos testes de análise de variância de 1 fator e ao teste de Tukey para comparações múltiplas (α=0,05). Nenhuma diferença estatística foi encontrada para os valores de contração de polimerização para Kalore (1,8 %) e Venus Diamond (1,7 %) (p≥0,05). Z250 apresentou estatisticamente maior contração de polimerização (2,0%). Kalore apresentou estatisticamente maior GC (60,8%) que Venus Diamond (49,5%) e Z250 (49,6%). Nenhuma diferença estatística foi encontrada para as propriedades RF e MY entre Venus Diamond e Z250. Kalore apresentou os menores valores estatisticos para FS e MY (p≥0,05). O monômero novelar parece reduzir a contração de polimerização sem afetar as propriedades físico-químicas avaliadas das resinas compostas de forma mais adequada que a utilização de monômeros do tipo crosslinker.

Integração Periodontia/Dent¡stica na restauração estatica anterior / Integration between Periodontics on anterior aesthetic restoration

A discrepƒncia da margem gengival somada a pr¢teses muito opacas e restaura‡ães insatisfat¢rias podem comprometer completamente a harmonia de um sorriso. Ferramentas como fotografia odontol¢gica, planejamento reverso e advento da Odontologia adesiva sÆo de vital importƒncia em um caso de reabilita‡Æo est‚tica do sorriso. No caso apresentado ‚ mostrado como essas ferramentas podem auxiliar um bom planejamento e desenvolvimento do caso, garantindo resultados s¢lidos e previs¡veis. Foram utilizadas t‚cnicas de an lise dentofacial, enceramento diagn¢stico, moke-up, gengivectomia, clareamento dental e finalizado com facetas e coroas em dissilicato de l¡tio. Seguindo um protocolo de planejamento reverso ‚ poss¡vel obter resultados de excelˆncia envolvendo menos elementos dentais, com menor desgaste e est‚tica natural.

Gingival margin discrepancy plus opaque and unsatisfactory dental restorations can compromise significantly the harmony of the smile. Tools such as dental photography, reverse planning and the advent of adhesive dentistry are for the aesthetic rehabilitation of the smile. The reported case shows how these tools can aid proper planning and development of the case, ensuring solid and predictable results. Techniques such as dentofacial analysis, wax-up, moke-up, gingivectomy, dental bleaching, and lithium disilicate crowns and veneers were used in the following case. When the reverse planning protocol is followed it is possible to obtain excellent results involving less dental elements, with minor dental wear and natural aesthetics.

Contorno cosmético: estética sem restauração / Cosmetic contour: esthetic without restoration

O desgaste irregular dos dentes, especialmente dos anteriores, além de uma diversidade de formatos anatômicos, pode acarretar em desarranjos estéticos do sorriso. Dessa forma, o contorno cosmético é um procedimento estético que implica em desgaste irreversível da estrutura dentária com pontas diamantadas e discos de acabamento, visando corrigir os parâmetros de estética e reflexão da luz dos dentes anteriores e pré-molares. Nesse sentido, todos os passos para a realização do contorno cosmético são críticos e de extrema importância. O objetivo desse artigo é apresentar, através do relato de um caso clínico, a confecção de uma remodelação cosmética do sorriso guiada por princípios de ilusão de óptica baseados em mínimos desgastes em esmalte dentário, garantindo uma previsibilidade estética do sorriso

Irregular dental wear, especially from the anterior teeth, and the various anatomic shapes can lead to an esthetic breakdown of the smile. So, cosmetic contouring is an esthetic approach which implies irreversible dental abrasion by diamond burs and fnishing disks in order to correct the esthetic parameters and light reflection of anterior teeth and pre-molars. In this sense, all steps for the cosmetic contouring procedure are critical and very important. The aim of this work was to present a case report that shows the cosmetic smile remodeling guided by principles of optical illusion based on minimal dental abrasion, ensuring a predictable esthetic smile.

Influence of etching time and bonding strategies on the microshear bond strength of self- and light-cured pit-and-fissure sealants

This study evaluated the impact of extended etching and bonding strategies on the microshear bond strength of three sealant materials. Two pit-and-fissure sealants [FluroShield, Dentsply (light-cured) and AlphaSeal, DFL (self-cured)] and one light-cured flowable composite resin (Permaflo, Ultradent) were evaluated according to different enamel etching times (15 s or 30 s) and bonding procedures (no adhesive application, application of primer/hydrophobic resin or hydrophobic resin only). Intact enamel blocks were obtained from bovine teeth and sealed via the tested protocols. After 24 h, the microshear bond strength test was performed in a universal testing machine at a crosshead speed of 0.5 mm/min. Failure modes were classified by stereomicroscopy. Data were submitted to a three-way ANOVA and to Tukey's test (α=0.05). There was no statistically significant difference (p>0.05) among the materials. Permaflo showed higher bond strength when etched for 30 s alone. Enamel overetching decreased the bond strength of the light-cured sealant. Primer/bond previous treatment improved bond performance for AlphaSeal. In conclusion, from the tested conditions, all sealant materials presented similar bond strength values in relation to bonding protocol and etching time. The flowable composite can be used as a pit-and-fissure sealant. The use of a three-step adhesive system was essential for the self-cured sealant application.

Este trabalho avaliou o impacto de tempos aumentados de condicionamento ácido e da estratégia adesiva na resistência de união por microcisalhamento de três materiais utilizados como selantes de fóssulas e fissuras. Dois tradicionais selantes, [FluroShield, Dentsply (fotoativado) e AlphaSeal, DFL (quimicamente ativado)] e uma resina composta de baixa viscosidade (Permaflo, Ultradent) foram utilizados de acordo com diferentes tempos de condicionamento ácido (15 s e 30 s) e diferentes estratégias de união (sem aplicação de sistema adesivo, aplicação de um primer + resina hidrófoba, e aplicação apenas de uma resina hidrófoba). Fragmentos de esmalte intacto foram obtidos de incisivos bovinos e os materiais foram aplicados respeitando-se os protocolos anteriormente descritos. Após 24 h, o teste de microcisalhamento foi executado utilizando-se uma máquina de ensaio universal, com velocidade de 0,5 mm/min. O padrão de fratura foi classificado com auxílio de lupa estereoscópica. Os dados foram submetidos aos testes ANOVA a três critérios e de Tukey (α=0.05). Não houve diferenças estatisticamente significantes entre os materiais. Permaflo apresentou maior resistência de união quando o esmalte foi condicionado por 30 s apenas. O sobrecondicionamento do esmalte diminuiu a resistência de união do selante fotopolimerizável. O tratamento prévio do esmalte com primer + resina hidrófoba melhorou a performance adesiva para o AlphaSeal. Todos os materiais apresentaram valores de resistência de união estatisticamente similares em relação ao protocolo adesivo e ao tempo de condicionamento ácido. A resina composta de baixa viscosidade poderá ser utilizada como selante de fóssulas e fissuras. A aplicação de um sistema adesivo de três passos é essencial durante o selamento com selante quimicamente ativado.

Resolução estética: naturalidade com coroas cerâmicas / Esthetic solution: nature-like results with ceramic crowns

A valorização da estética do sorriso favorece o interesse pelos materiais cerâmicos na reabilitação dental, em função de resultados naturais e fáceis de ser alcançados. As propriedades ópticas semelhantes às da estrutura dentária, associadas à capacidade mecânica proporcionada pelas cerâmicas reforçadas (metal free), têm possibilitado resoluções estéticas sem comprometimento funcional. Dessa forma, este relato de caso clínico tem por objetivo descrever uma resolução estética com indicação de coroas cerâmicas metal free para resolução estético-funcional do sorriso, discutindo indicações e características, assim como as técnicas empregadas para o uso desses materiais

The appreciation of the smile esthetics favors the interest for ceramic materials used oral rehabilitation, since the clinician can achieve natural, esthetic results. Optical properties similar to tooth structure in association with the mechanical strength provided by reinforced all-ceramic restorations produce esthetic results without functional impairment. Thus, the aim of this case report is to describe an esthetic indication of all-ceramic crowns to reach esthetic, functional smile resolution and to discuss its indications and characteristics, and the technique used to these materials

Reabilitação estética anterior com coroas totais metal-free utilizando-se cerâmica reforçada por dissilicato de lítio / Esthetic anterior rehabilitation with metal-free crowns: lithium dissilicate ceramics

O desgaste dos dentes anteriores pode acarretar desarranjos funcionais, assim como desarmonia estética. Devido a suas ótimas propriedades ópticas e biomecânicas, as cerâmicas dentais têm sido cada vez mais utilizadas na resolução de problemas relacionados à estética do sorriso. As cerâmicas reforçadas por dissilicato de lítio são opções viáveis para esse tipo de reabilitação. Nesse sentido, todos os passos para realização da restauração indireta cerâmica são críticos e de extrema importância. O objetivo deste artigo é apresentar, por meio do relato de um caso clínico, a confecção de restaurações de dentes ântero-superiores com severo desgaste, com coroas totais em cerâmica reforçada por dissilicato de lítio. Para a realização de casos com previsibilidade e sucesso, as diferentes etapas de confecção são detalhadas e minuciosamente discutidas, e demonstram-se os pontos chave desse procedimento...

Wear of anterior teeth can cause functional disorders, and esthetic disharmony. Due to their excellent optical and biomechanical properties, dental ceramics are increasingly used to solve esthetic problems. Reinforced ceramics, e.g. those composed by lithium disilicate, are feasible options for this type of rehabilitation. Therefore, every step involving the fabrication of indirect ceramic restorations is critical. This article presented a case report of the restoration of maxillary anterior teeth with severe wear, using full crowns fabricated with lithium disilicate reinforced ceramics. The steps are described in detail and thoroughly discussed, demonstrating key concepts to achieve predictable, successful results...

Restauração estética direta de dente anterior fraturado: relato de caso clínico / Direct aesthetic restoration of fractured anterior teeth: case report

O protocolo restaurador direto com resina composta para dentes anteriores fraturados é um desafio na Odontologia Adesiva atual, já que existem vários compósitos à disposição no mercado, com características ópticas e mecânicas cada vez mais semelhantes às da estrutura dentária. Dessa forma, a técnica de estratificação em camadas de resina composta torna-se eficiente para uso na clínica odontológica. Nesse artigo, o caso clínico apresentado abordará a restauração estética de um incisivo medial fraturado, com o procedimento de estratificação de resina composta, trabalhando os conceitos de translucidez e opacidade para uma adequada reabilitação dentária de forma estética e funcional.

Uso de princípios de ilusão óptica no contorno cosmético: previsibilidade e excelência estética / Using principles of optical illusion for cosmetic recontouring: predictability and esthetic excellence

O contorno cosmético é uma técnica operatória que requer do profissional amplo conhecimento de estética e reflexão da luz, pois implica desgaste irreversível da estrutura dental sadia. Este artigo relata um caso clínico de contorno cosmético que ilustra as possibilidades de remodelação estética do sorriso guiadas por princípios de ilusão de óptica, na qual foi possível, mediante a realização de desgastes em esmalte, obter resultados satisfatórios com previsibilidade.

Cosmetic recontouring is a technique that demands comprehensive skills and knowledge about esthetics light dynamics by the professional, since irreversible reduction of tooth sound structure is required. This paper is a case report of the cosmetic contouring showing the possibilities of esthetic recontouring of the smile following principles of optical illusion, from which it was possible through enamel reduction to achieve satisfactory, predictable results.

Análise crítica dos métodos utilizados para determinar o surto de crescimento puberal pelos especialistas em ortodontia / Critical analysis of the used methods occasion to determine it of puberal growth for the specialists in orthodontics

Avaliar o surto de crescimento puberal (SCP) é importante na prática clínica ortodôntica, visto que o crescimento corporal que acontece nessa fase pode atuar como um excelente coadjuvante no tratamento. Esse estudo se propôs a analisar quais e como os métodos são utilizados pelos especialistas em ortodontia, da cidade de Salvador (Bahia), para avaliar o SCP. Foram enviados questionários com perguntas fechadas e abertas a todos os dentistas registrados no CROBA como especialistas em ortodontia. O universo foi composto de 90 ortodontistas e, desses, 67 responderam o questionário, constituindo uma amostra em que 64,1% dos informantes pertenciam ao sexo feminino. Os resultados mostram que todos os entrevistados concordaram ser necessário verificar o SCP e, desses, 94% indicaram seu uso para casos específicos como: pacientes em crescimento, distúrbios de crescimento ósseo, tratamento ortocirúrgico e (ou) ortopédicos, casos limítrofes, dúvidas sobre o estágio de desenvolvimento. Quanto ao método utilizado, houve uma predominância da análise carpal, seguida da análise das vértebras cervicais, dental e caracteres sexuais secundários. Nenhum dos entrevistados vinculou o SCP apenas à idade cronológica. Entretanto, quando solicitados a listar nomes dos métodos preferidos e dificuldades encontradas, foi grande o número de entrevistados que deixou de responder as perguntas. Tal fato faz concluir ser necessária uma maior divulgação dos métodos de análise do SCP, principalmente da análise das vértebras cervicais, que é o mais recente.

Displasia cemento-óssea florida: relato de caso / Florid cemento-osseous dysplasia: case report

A displasia cemento-óssea florida (DCOF) é uma entidade incomum, benigna, frequentemente assintomátíca, limitada aos ossos gnáticos e acomete frequentemente mulheres negras acima de 40 anos. Nos casos com sintomatologia dolorosa, há uma associação com osteomielite crônica, provavelmente decorrente de infecçãso secundária. Esse tipo de lesão possui aspectos radiográficos e histopatológicos encontrados em outras patologias, como osteomielite esclerosante difusa e doença de Paget do osso. O objetivo desse estudo foi revisar a literatura acerca desta lesão, além de relatar um caso clínico de DCOF associada à osteomielite crônica. O exame clínico-anamnésico realizado com destreza, associado aos métodos complementares imagenológicos traz informações importantes para o diagnóstico dessa patologia, modulando os cuidados com os procedimentos cirúrgicos que muitas vezes são necessários para a terapêutica das complicações infecciosas. Por outro lado, procedimentos como exodontias, podem vir a favorecê-las, agravando assim, o quadro clínico do paciente.

Florid cemento-osseous dysplasia (FCOD) is an uncommon benign entity, frequently without painful sintomatology, limited to gnatic bones and occurs frequently in black women, above of 40 years. In cases with painful sintomatology, it has an association with chronic osteomielitis, probably decurrent of secondary infection. This kind of lesion has radiographic and histopathologic aspects found in others pathologies, as diffuse esclerosant osteomielitis and Paget's disease of the bone. The aim of this study was to revise the literature about this lesion, and report a clinical case of FCOD associated with chronic osteomielitis. Physical-anamnesic examination carried through with dexterity, associated to imagenologic complementary methods can bring important information for the diagnosis of this pathology, modulating the cares with the surgical procedures that many times are necessary for the therapeutics of the infectious complications. On the other hand, procedures as exodonties, can come to favor them, thus aggravating, the clinical aspects of the patient.

Influence of the curing method on the post-polymerization shrinkage stress of a composite resin

The aim of this study was to evaluate the effect of different curing methods on the stress generated by the polymerization shrinkage of a restorative composite in two moments: immediately after light exposure and after 5 min. Photoactivation was performed using two different light sources: (1) xenon plasma arc (PAC) light (1,500 mW/cm2 - 3s) and (2) a quartz-tungsten-halogen (QTH) light with three light-curing regimens: continuous exposure (40 s at 800 mW/cm2 - CL); soft-start (10 s at 150 mW/cm2 and 30 s at 800 mW/cm2 - SS) and intermittent light [cycles of 4 s (2 s with light on at 600 mW/cm2 and 2 s of light off), for 80s - IL]. The composite resin was applied between two 5-mm diameter metallic rods, mounted in a servohydraulic machine. The maximum stress was recorded immediately after light exposure (FF) and after 5 min (5F). The results were submitted to ANOVA and Tukey's test (5 percent). For each method, the results obtained in FF and 5F were, respectively: CL (3.58 and 4.46 MPa); SS (2.99 and 4.36 MPa); IL (3.11 and 4.32 MPa) and PAC (0.72 and 3.27 MPa). The stress generated by the polymerization shrinkage during light exposure can be associated with the photoactivation method used. A significant increase in the stress level was observed during the post-curing period up to 5 min, for all evaluated methods.